Abstract:Because of suitable mechanical properties, good bio-compatibility and biodegradability, Mg and its alloys are expected to become a new class of medical implant materials. Mg and its alloy were used as medical material a long time ago, but the over fast degradation rate restricted their application. Recently, with the development of metallurgy and surface modification technology, researches on the medical applications of Mg and its alloy are rapidly developed. This paper briefly reviewed the current research and development status of Mg-based metals as implant materials, described their advantages and disadvantages for applications, and prospected the developing tendency for their applications as medical materials.
于晓明,谭丽丽,万鹏,杨柯. 医用镁及镁合金研究进展[J]. 中国医疗设备, 2015, 30(9): 1-5.
YU Xiao-ming, TAN Li-li, WAN Peng, YANG Ke. Progress in Research of Mg and Mg Alloys for Medical Applications. China Medical Devices, 2015, 30(9): 1-5.
Katti KS.Biomaterials in total joint replacement[J].Colloid Surface B,2004,39:133-142.
[43]
Lin X,Tan L,Wan P,et al.Characterization of micro-arc oxidation coating post-treated by hydrofluoric acid on biodegradable ZK60 magnesium alloy[J].Surf Coat Tech,2013,232(10):899-805.
[43]
Lin X,Tan L,Wan P,et al.Characterization of micro-arc oxidation coating post-treated by hydrofluoric acid on biodegradable ZK60 magnesium alloy[J].Surf Coat Tech,2013,232(10):899-805.
[43]
Lin X,Tan L,Wan P,et al.Characterization of micro-arc oxidation coating post-treated by hydrofluoric acid on biodegradable ZK60 magnesium alloy[J].Surf Coat Tech,2013,232(10):899-805.
[34]
Tan L,Wang Q,Geng F,et al.Preparation and characterization of Ca-P coating on AZ31 magnesium alloy[J].T Nonferr Metal Soc,20(S2):s648-s654.
[2]
Katti KS.Biomaterials in total joint replacement[J].Colloid Surface B,2004,39:133-142.
[3]
Tan L,Yu X,Wan P,et al.Biodegradable Materials for Bone Repairs:A Review[J].J Mater Sci Technol,2013,29(6):503-513.
[3]
Tan L,Yu X,Wan P,et al.Biodegradable Materials for Bone Repairs:A Review[J].J Mater Sci Technol,2013,29(6):503-513.
[4]
Staiger MP,Pietak AM,Huadmai J,et al.Magnesium and its alloys as orthopedic biomaterials:a review[J].Biomaterials,2006,27(9):1728-1734.
[5]
Witte F,Kaese V,Haferkamp H,et al.In vivo corrosion of four magnesium alloys and the associated bone response[J].Biomaterials,2005,26(17):3557-3563.
[6]
Xu L,Yu G,Zhang E,et al.In vivo corrosion behavior of Mg-Mn-Zn alloy for bone implant application[J].J Biomed Mater Res A,2007,83(3):703-711.
[7]
Yamada Y,Shimojima K,Sakaguchi Y,et al.Processing of an open-cellular AZ91 magnesium alloy with a low density of 0.05 g/cm3[J].J Mater Sci,1999,18(18):1477-1480.
[8]
Wen CE,Yamada Y,Shimojima K,et al.Compressibility of porous magnesium foam:dependency on porosity and pore size[J].Mater Lett,2004,58(3):357-360.
Tan L,Gong M,Zheng F,et al.Study on compression behavior of porous magnesium used as bone tissue engineering scaffolds[J].Biomed Mater,2009,4(1):1246-1253.
Geng F,Tan L,Zhang B,et al.Study on β-TCP Coated Porous Mg as a Bone Tissue Engineering Scaffold Material[J].J Mater Sci Technol,2009,25(1):123-129.
[21]
Li J,Zheng F,Qiu X,et al.Finite element analyses for optimization design of biodegradable magnesium alloy stent[J].Mater Sci Eng C Mater Biol Appl,2014,42:705-714.
Xu L,Yu G,Zhang E,et al.In vivo corrosion behavior of Mg-Mn-Zn alloy for bone implant application[J].J Biomed Mater Res A,2007,83(3):703-711.
[7]
Yamada Y,Shimojima K,Sakaguchi Y,et al.Processing of an open-cellular AZ91 magnesium alloy with a low density of 0.05 g/cm3[J].J Mater Sci,1999,18(18):1477-1480.
[7]
Yamada Y,Shimojima K,Sakaguchi Y,et al.Processing of an open-cellular AZ91 magnesium alloy with a low density of 0.05 g/cm3[J].J Mater Sci,1999,18(18):1477-1480.
[8]
Wen CE,Yamada Y,Shimojima K,et al.Compressibility of porous magnesium foam:dependency on porosity and pore size[J].Mater Lett,2004,58(3):357-360.
Tan L,Gong M,Zheng F,et al.Study on compression behavior of porous magnesium used as bone tissue engineering scaffolds[J].Biomed Mater,2009,4(1):1246-1253.
[13]
Tan L,Gong M,Zheng F,et al.Study on compression behavior of porous magnesium used as bone tissue engineering scaffolds[J].Biomed Mater,2009,4(1):1246-1253.
[15]
Geng F,Tan L,Zhang B,et al.Study on β-TCP Coated Porous Mg as a Bone Tissue Engineering Scaffold Material[J].J Mater Sci Technol,2009,25(1):123-129.
Li H,Zhong H,Xu K,et al.Enhanced Efficacy of Sirolimus-Eluting Bioabsorbable Magnesium Alloy Stents in the Prevention of Restenosis[J].J Endovasc Ther,2011,18(3):407-415.
[21]
Li J,Zheng F,Qiu X,et al.Finite element analyses for optimization design of biodegradable magnesium alloy stent[J].Mater Sci Eng C Mater Biol Appl,2014,42:705-714.
Li H,Zhong H,Xu K,et al.Enhanced Efficacy of Sirolimus-Eluting Bioabsorbable Magnesium Alloy Stents in the Prevention of Restenosis[J].J Endovasc Ther,2011,18(3):407-415.
[17]
Li H,Zhong H,Xu K,et al.Enhanced Efficacy of Sirolimus-Eluting Bioabsorbable Magnesium Alloy Stents in the Prevention of Restenosis[J].J Endovasc Ther,2011,18(3):407-415.
[18]
Wu W,Gastaldi D,Yang K,et al.Finite element analyses for design evaluation of biodegradable magnesium alloy stents in arterial vessels[J].Mater Sci Eng B-Adv,2011,176(20):1733-1740.
[18]
Wu W,Gastaldi D,Yang K,et al.Finite element analyses for design evaluation of biodegradable magnesium alloy stents in arterial vessels[J].Mater Sci Eng B-Adv,2011,176(20):1733-1740.
[19]
Wu W,Chen S,Gastaldi D,et al.Experimental data confirm numerical modeling of the degradation process of magnesium alloys stents[J].Acta Biomater,2013,9(10):8730-8739.
[19]
Wu W,Chen S,Gastaldi D,et al.Experimental data confirm numerical modeling of the degradation process of magnesium alloys stents[J].Acta Biomater,2013,9(10):8730-8739.
[20]
Li J,Mao Z,Zheng F,et al.Simulation study on uneven expansion behaviour of biodegradable magnesium alloy stents by finite element analysis[J].J Mater Sci Technol,2014,30(5):527-533.
[21]
Li J,Zheng F,Qiu X,et al.Finite element analyses for optimization design of biodegradable magnesium alloy stent[J].Mater Sci Eng C Mater Biol Appl,2014,42:705-714.
[22]
Wan P,Wu J,Tan L,et al.Research on super-hydrophobic surface of biodegradable magnesium alloys used for vascular stents[J].Mater Sci Eng C Mater Biol Appl,2013,33(5):2885-2890.
[22]
Wan P,Wu J,Tan L,et al.Research on super-hydrophobic surface of biodegradable magnesium alloys used for vascular stents[J].Mater Sci Eng C Mater Biol Appl,2013,33(5):2885-2890.
[23]
Lin X,Tan L,Wang Q,et al.In vivo degradation and tissue compatibility of ZK60 magnesium alloy with micro-arc oxidation coating in a transcortical model[J].Mater Sci Eng C Mater Biol Appl,2013,33(7):3881-3888.
Tan L,Wang Q,Geng F,et al.Preparation and characterization of Ca-P coating on AZ31 magnesium alloy[J].T Nonferr Metal Soc,20(S2):s648-s654.
[18]
Wu W,Gastaldi D,Yang K,et al.Finite element analyses for design evaluation of biodegradable magnesium alloy stents in arterial vessels[J].Mater Sci Eng B-Adv,2011,176(20):1733-1740.
[19]
Wu W,Chen S,Gastaldi D,et al.Experimental data confirm numerical modeling of the degradation process of magnesium alloys stents[J].Acta Biomater,2013,9(10):8730-8739.
[20]
Li J,Mao Z,Zheng F,et al.Simulation study on uneven expansion behaviour of biodegradable magnesium alloy stents by finite element analysis[J].J Mater Sci Technol,2014,30(5):527-533.
[20]
Li J,Mao Z,Zheng F,et al.Simulation study on uneven expansion behaviour of biodegradable magnesium alloy stents by finite element analysis[J].J Mater Sci Technol,2014,30(5):527-533.
[22]
Wan P,Wu J,Tan L,et al.Research on super-hydrophobic surface of biodegradable magnesium alloys used for vascular stents[J].Mater Sci Eng C Mater Biol Appl,2013,33(5):2885-2890.
[23]
Lin X,Tan L,Wang Q,et al.In vivo degradation and tissue compatibility of ZK60 magnesium alloy with micro-arc oxidation coating in a transcortical model[J].Mater Sci Eng C Mater Biol Appl,2013,33(7):3881-3888.
[23]
Lin X,Tan L,Wang Q,et al.In vivo degradation and tissue compatibility of ZK60 magnesium alloy with micro-arc oxidation coating in a transcortical model[J].Mater Sci Eng C Mater Biol Appl,2013,33(7):3881-3888.
[24]
Zhang Q,Lin X,Qi Z,et al.Magnesium Alloy for Repair of Lateral Tibial Plateau Defect in Minipig Model[J].J Mater Sci Technol,2013,29(6):539-544.
[24]
Zhang Q,Lin X,Qi Z,et al.Magnesium Alloy for Repair of Lateral Tibial Plateau Defect in Minipig Model[J].J Mater Sci Technol,2013,29(6):539-544.
[24]
Zhang Q,Lin X,Qi Z,et al.Magnesium Alloy for Repair of Lateral Tibial Plateau Defect in Minipig Model[J].J Mater Sci Technol,2013,29(6):539-544.
[25]
Qi Z R,Zhang Q,Tan LL,et al.Comparison of degradation behavior and the associated bone response of ZK60 and PLLA in vivo[J].J Biomed Mater Res A,2014,102(5):1255-1263.
[25]
Qi Z R,Zhang Q,Tan LL,et al.Comparison of degradation behavior and the associated bone response of ZK60 and PLLA in vivo[J].J Biomed Mater Res A,2014,102(5):1255-1263.
[25]
Qi Z R,Zhang Q,Tan LL,et al.Comparison of degradation behavior and the associated bone response of ZK60 and PLLA in vivo[J].J Biomed Mater Res A,2014,102(5):1255-1263.
[26]
Tan L,Wang Q,Lin X,et al.Loss of mechanical properties in vivo and bone-implant interface strength of AZ31B magnesium alloy screws with Si-containing coating[J].Acta Biomater,2014,10(5):2333-2340.
[26]
Tan L,Wang Q,Lin X,et al.Loss of mechanical properties in vivo and bone-implant interface strength of AZ31B magnesium alloy screws with Si-containing coating[J].Acta Biomater,2014,10(5):2333-2340.
[26]
Tan L,Wang Q,Lin X,et al.Loss of mechanical properties in vivo and bone-implant interface strength of AZ31B magnesium alloy screws with Si-containing coating[J].Acta Biomater,2014,10(5):2333-2340.
[28]
Zhang Y,Ren L,Li M,et al.Preliminary Study on Cytotoxic Effect of Biodegradation of Magnesium on Cancer Cells[J].J Mater Sci Technol,2012,28(9):769-772.
[28]
Zhang Y,Ren L,Li M,et al.Preliminary Study on Cytotoxic Effect of Biodegradation of Magnesium on Cancer Cells[J].J Mater Sci Technol,2012,28(9):769-772.
[28]
Zhang Y,Ren L,Li M,et al.Preliminary Study on Cytotoxic Effect of Biodegradation of Magnesium on Cancer Cells[J].J Mater Sci Technol,2012,28(9):769-772.
[29]
Zhu L,Wan P,Duan J,et al.An alternative magnesium-based root canal disinfectant:preliminary study of its efficacy against Enterococcus faecalis and Candida albicans in vitro[J].Prog Nat Sci,2014,24(5):441-445.
[29]
Zhu L,Wan P,Duan J,et al.An alternative magnesium-based root canal disinfectant:preliminary study of its efficacy against Enterococcus faecalis and Candida albicans in vitro[J].Prog Nat Sci,2014,24(5):441-445.
[29]
Zhu L,Wan P,Duan J,et al.An alternative magnesium-based root canal disinfectant:preliminary study of its efficacy against Enterococcus faecalis and Candida albicans in vitro[J].Prog Nat Sci,2014,24(5):441-445.
[30]
Liu C,Wan P,Tan LL,et al.Preclinical investigation of an innovative magnesium-based bone graft substitute for potential orthopaedic applications[J].JOT,2014,2(3):139-148.
[30]
Liu C,Wan P,Tan LL,et al.Preclinical investigation of an innovative magnesium-based bone graft substitute for potential orthopaedic applications[J].JOT,2014,2(3):139-148.
[30]
Liu C,Wan P,Tan LL,et al.Preclinical investigation of an innovative magnesium-based bone graft substitute for potential orthopaedic applications[J].JOT,2014,2(3):139-148.
Yan T,Tan L,Xiong D,et al.Fluoride treatment and in vitro corrosion behavior of an AZ31B magnesium alloy[J].Mat Sci Eng C,2010,30(5):740-748.
[35]
Wang Q,Tan LL, Zhang Q,et al.Precipitation control and mechanical property of Ca-P coated AZ31B alloy for biomedical application[J].Biomed Eng-App Bas C,2011,23(3):193-203.
[35]
Wang Q,Tan LL, Zhang Q,et al.Precipitation control and mechanical property of Ca-P coated AZ31B alloy for biomedical application[J].Biomed Eng-App Bas C,2011,23(3):193-203.
[36]
Wang Q,Tan L,Xu W,et al.Dynamic behaviors of a Ca-Pcoated AZ31B magnesium alloy during in vitro and in vivo degradations[J].Mat Sci Eng B,2011,176(20):1718-1726.
[36]
Wang Q,Tan L,Xu W,et al.Dynamic behaviors of a Ca-Pcoated AZ31B magnesium alloy during in vitro and in vivo degradations[J].Mat Sci Eng B,2011,176(20):1718-1726.
[37]
Lu Y,Wan P,Tan L,et al.Preliminary study on a bioactive Sr containing Ca-P coating on pure magnesium by a two-step procedure[J].Surf Coat Tech,2014,252(9):79-86.
[37]
Lu Y,Wan P,Tan L,et al.Preliminary study on a bioactive Sr containing Ca-P coating on pure magnesium by a two-step procedure[J].Surf Coat Tech,2014,252(9):79-86.
Yan T,Tan L,Xiong D,et al.Fluoride treatment and in vitro corrosion behavior of an AZ31B magnesium alloy[J].Mat Sci Eng C,2010,30(5):740-748.
[33]
Yan T,Tan L,Xiong D,et al.Fluoride treatment and in vitro corrosion behavior of an AZ31B magnesium alloy[J].Mat Sci Eng C,2010,30(5):740-748.
[34]
Tan L,Wang Q,Geng F,et al.Preparation and characterization of Ca-P coating on AZ31 magnesium alloy[J].T Nonferr Metal Soc,20(S2):s648-s654.
[35]
Wang Q,Tan LL, Zhang Q,et al.Precipitation control and mechanical property of Ca-P coated AZ31B alloy for biomedical application[J].Biomed Eng-App Bas C,2011,23(3):193-203.
[36]
Wang Q,Tan L,Xu W,et al.Dynamic behaviors of a Ca-Pcoated AZ31B magnesium alloy during in vitro and in vivo degradations[J].Mat Sci Eng B,2011,176(20):1718-1726.
[37]
Lu Y,Wan P,Tan L,et al.Preliminary study on a bioactive Sr containing Ca-P coating on pure magnesium by a two-step procedure[J].Surf Coat Tech,2014,252(9):79-86.
[38]
Geng F,Tan LL,Jin XX,et al.The Preparation,Cytocompatibility,And In Vitro Biodegradation Study Of Pure β-Tcp On Magnesium[J].J Mater Sci-Mater M,2009,20(5):1149-1157.
[38]
Geng F,Tan LL,Jin XX,et al.The Preparation,Cytocompatibility,And In Vitro Biodegradation Study Of Pure β-Tcp On Magnesium[J].J Mater Sci-Mater M,2009,20(5):1149-1157.
[39]
Lu YJ,Tan LL,Xiang HL,et al.Fabrication and Characterization of Ca-Mg-P Containing Coating on Pure Magnesium[J].J Mater Sci Tech,2012,28(7):636-641.
[40]
Lu Y,Tan L,Xiang H,et al.Study on corrosion resistance of pure magnesium with CaSiO3 contained coating in NaCl solution[J].Acta Metall Sin-Engl,2012,25(4):287-294.
[41]
Yang X,Li M,Lin X,et al.Enhanced in vitro biocompatibility/bioactivity of biodegradable Mg-Zn-Zr alloy by micro-arc oxidation coating contained Mg2SiO4[J].Surf Coat Tech,2013,233:65-73.
[42]
Lin X,Yang K,Tan L,et al.In vitro degradation process and bio-compatibility of ZK60 magnesium alloy with forsterite- containing micro-arc oxidation coating[J].Acta Biomater,2013,9:8631-8642.
[38]
Geng F,Tan LL,Jin XX,et al.The Preparation,Cytocompatibility,And In Vitro Biodegradation Study Of Pure β-Tcp On Magnesium[J].J Mater Sci-Mater M,2009,20(5):1149-1157.
[39]
Lu YJ,Tan LL,Xiang HL,et al.Fabrication and Characterization of Ca-Mg-P Containing Coating on Pure Magnesium[J].J Mater Sci Tech,2012,28(7):636-641.
[39]
Lu YJ,Tan LL,Xiang HL,et al.Fabrication and Characterization of Ca-Mg-P Containing Coating on Pure Magnesium[J].J Mater Sci Tech,2012,28(7):636-641.
[40]
Lu Y,Tan L,Xiang H,et al.Study on corrosion resistance of pure magnesium with CaSiO3 contained coating in NaCl solution[J].Acta Metall Sin-Engl,2012,25(4):287-294.
[40]
Lu Y,Tan L,Xiang H,et al.Study on corrosion resistance of pure magnesium with CaSiO3 contained coating in NaCl solution[J].Acta Metall Sin-Engl,2012,25(4):287-294.
[41]
Yang X,Li M,Lin X,et al.Enhanced in vitro biocompatibility/bioactivity of biodegradable Mg-Zn-Zr alloy by micro-arc oxidation coating contained Mg2SiO4[J].Surf Coat Tech,2013,233:65-73.
[41]
Yang X,Li M,Lin X,et al.Enhanced in vitro biocompatibility/bioactivity of biodegradable Mg-Zn-Zr alloy by micro-arc oxidation coating contained Mg2SiO4[J].Surf Coat Tech,2013,233:65-73.
[42]
Lin X,Yang K,Tan L,et al.In vitro degradation process and bio-compatibility of ZK60 magnesium alloy with forsterite- containing micro-arc oxidation coating[J].Acta Biomater,2013,9:8631-8642.
[42]
Lin X,Yang K,Tan L,et al.In vitro degradation process and bio-compatibility of ZK60 magnesium alloy with forsterite- containing micro-arc oxidation coating[J].Acta Biomater,2013,9:8631-8642.
[44]
Lin X,Yang X,Tan L,et al.In vitro degradation and biocompatibility of a strontium-containing micro-arc oxidation coating on the biodegradable ZK60 magnesium alloy[J].Appl Surf Sci,2014,288(2):718-726.
[44]
Lin X,Yang X,Tan L,et al.In vitro degradation and biocompatibility of a strontium-containing micro-arc oxidation coating on the biodegradable ZK60 magnesium alloy[J].Appl Surf Sci,2014,288(2):718-726.
[44]
Lin X,Yang X,Tan L,et al.In vitro degradation and biocompatibility of a strontium-containing micro-arc oxidation coating on the biodegradable ZK60 magnesium alloy[J].Appl Surf Sci,2014,288(2):718-726.
[45]
Lin X,Wang X,Tan L,et al.Effect of preparation parameters on the properties of hydroxyapatite containing micro-arc oxidation coating on biodegradable ZK60 magnesium alloy[J].Ceram Int,2014,40(7):10043-10051.
[45]
Lin X,Wang X,Tan L,et al.Effect of preparation parameters on the properties of hydroxyapatite containing micro-arc oxidation coating on biodegradable ZK60 magnesium alloy[J].Ceram Int,2014,40(7):10043-10051.